Stainless Steel Lost Wax Casting Common Material

Sebon is specialized in stainless steel lost wax casting suppy. The stainless steel precision casting products are widely used for auto-car components, Machinery & Pump Parts, Marine Parts, valve parts, pipe parts, etc.
Product Material
Normally produce withASTM A743/A743M Grade CF8, CF-8M, CF-3, CF-3M, ZG0Cr18Ni10, ZG0Cr18Ni9, ZG0Cr18Ni9Ti, ZG0Cr18Ni12Mo2Ti, ZG1Cr18Ni12Mo2Ti, etc.
Stainless Steel Types
We can nearly cast any type of stainless steel alloys. Depending on the different amount of unique elements and the quantity (%) of elements contained within the stainless steel, a unique stainless steel alloy can be created. Thanks to the large variation in compositions, countless stainless steel castings are possible. Below you will find a short overview of the stainless steel types that we cast most often.

Mat. no.	Symbol	Similar to	Heat treatment	Proof stress Rp0,2	Tensile strength (N/mm²)	Elongation (%)	Hardness
1.4008	GX7CrNiMo12-1	AISI 410	Refining	≥ 440	590-790	≈ 15	≥ 90 HRb
1.4027	GX20Cr14	-	Refining	≥ 400	590-790	≈ 15	18-50 HRc
1.4036	GX46Cr13	-	Refining	-	750-900	-	15-53 HRc
1.4059	GX22CrNi17	-	Refining	600- 750	800-950	≈ 8	22-50 HRc
1.4162	X2CrMnNiN21-5-1			-	-	-	-
1.4308	GX5CrNi19-10	AISI 304 / CF8				> 175	> 440	> 30	75-90 HRb
1.4309	GX2CrNi19-11	AISI 304L / CF3	Casting condition	> 210	440-460	> 30	70-80 HRb
1.4317	GX4CrNi13-4	-	Refining	> 650	800-1000	> 15	22-30 HRc
1.4408		GX5CrNiMi19-11-2		AISI 316 / CF8M		Solution annealing+ quench hardening		> 200	> 450	> 20	75-90 HRb
1.4409	GX2CrNiMi19-11-2	AISI 316L / CF3M	Solution annealing+ quench hardening	> 200	> 450	> 20	75-90 HRb
1.4468	GX2CrNiMoN25-6-3	-	Casting condition	-	> 650	> 22	> 92 HRb
1.4470	GX2CrNiMoN22-5-3		Normal annealing	> 450	680-880	> 30	> 93 HRb
1.4827	GX8CrNiNb19-10		Solution annealing+ quench hardening	> 175	> 440	> 20	75-95 HRb